Tensile behavior of lignocellulosic fiber reinforced polymer composites: Part I piassava/epoxy
The fibers extracted from the piassava palm tree, scientifically known as Attalea funifera, are among the stiffest lignocellulosic fibers being considered for polymer composite reinforcement. Characterization of piassava composites have been carried out for different polymeric matrices and mechanical tests. In this work the tensile properties of DGEBA/TETA epoxy matrix composites reinforced with up to 30% in volume of continuous and aligned piassava fibers were evaluated. Tensile specimens post-cured at 60ºC for 4 hours were room temperature tested and the corresponding fracture analyzed by scanning electrons microscopy. The results showed a decrease in both the tensile strength and the elastic modulus of the composites up to 30% with an increase at 40% of piassava fibers to values above those of the pure epoxy. The fracture analysis revealed a weak fiber/matrix interface, which could account for the comparative low performance of these composite in tensile tests up to 30% of volume fraction. The relatively large amount of stronger piassava fibers accounts for the better performance of the composite with 40% in volume fraction.
| Main Authors: | , , |
|---|---|
| Format: | Digital revista |
| Language: | English |
| Published: |
Laboratório de Hidrogênio, Coppe - Universidade Federal do Rio de Janeiro
2010
|
| Online Access: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1517-70762010000200015 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The fibers extracted from the piassava palm tree, scientifically known as Attalea funifera, are among the stiffest lignocellulosic fibers being considered for polymer composite reinforcement. Characterization of piassava composites have been carried out for different polymeric matrices and mechanical tests. In this work the tensile properties of DGEBA/TETA epoxy matrix composites reinforced with up to 30% in volume of continuous and aligned piassava fibers were evaluated. Tensile specimens post-cured at 60ºC for 4 hours were room temperature tested and the corresponding fracture analyzed by scanning electrons microscopy. The results showed a decrease in both the tensile strength and the elastic modulus of the composites up to 30% with an increase at 40% of piassava fibers to values above those of the pure epoxy. The fracture analysis revealed a weak fiber/matrix interface, which could account for the comparative low performance of these composite in tensile tests up to 30% of volume fraction. The relatively large amount of stronger piassava fibers accounts for the better performance of the composite with 40% in volume fraction. |
|---|