Effect of the Brazilian thermal modification process on the chemical composition of Eucalyptus grandis juvenile wood: Part 1: Cell wall polymers and extractives contents
This article reports the first study of the influence of the Brazilian process of thermal modification called VAP HolzSysteme® on the chemical composition of Eucalyptus wood. Flatsawn boards of Eucalyptus grandis juvenile wood were tested for four treatment levels: untreated and thermally modified at final cycle temperatures of 140, 160 and 180 °C. Chemical analyses were carried out according to the standards of the Technical Association of the Pulp and Paper Industry and encompassed total extractives, insoluble lignin, holocellulose (cellulose + hemicelluloses) and solvent soluble extractives in water (cold and hot) and ethanol:toluene (1:2 v.v.) mixture. The chemical composition of thermally modified Eucalyptus grandis juvenile wood was significantly changed by the VAP HolzSysteme® process compared to untreated wood. Only the wood thermally modified at final cycle temperature of 180 °C was significantly different for all the chemical analyses performed compared to untreated wood.
| Main Authors: | , , , , |
|---|---|
| Format: | Digital revista |
| Language: | English |
| Published: |
Universidad del Bío-Bío
2016
|
| Online Access: | http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0718-221X2016000200005 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This article reports the first study of the influence of the Brazilian process of thermal modification called VAP HolzSysteme® on the chemical composition of Eucalyptus wood. Flatsawn boards of Eucalyptus grandis juvenile wood were tested for four treatment levels: untreated and thermally modified at final cycle temperatures of 140, 160 and 180 °C. Chemical analyses were carried out according to the standards of the Technical Association of the Pulp and Paper Industry and encompassed total extractives, insoluble lignin, holocellulose (cellulose + hemicelluloses) and solvent soluble extractives in water (cold and hot) and ethanol:toluene (1:2 v.v.) mixture. The chemical composition of thermally modified Eucalyptus grandis juvenile wood was significantly changed by the VAP HolzSysteme® process compared to untreated wood. Only the wood thermally modified at final cycle temperature of 180 °C was significantly different for all the chemical analyses performed compared to untreated wood. |
|---|