New Synthesis Method for a Core-Shell Composite Based on α-Bi2O3 @PPy and its Electrochemical Behavior as Supercapacitor Electrode
New composite based on polypyrrole (PPy) and bismuth oxide (α-Bi2O3) was investigated as supercapacitor electrode. The α-Bi2O3 was obtained by hydrothermal route at 500 ºC for 2 h. Cyclic voltammetry was used to electropolymerize PPy on graphite electrode (GE) or on GE/α-Bi2O3. The X-ray diffraction profile of Bi2O3 revealed the α-Bi2O3 monoclinic structure with space group P21/c.The scanning and transmission electron microscopy images showed that PPy coated α-Bi2O3. Raman spectra showed that PPy inhomogeneously coated α-Bi2O3, but it was still possible to obtain a α-Bi2O3 @PPy core-shell hybrid composite with highly ordered α-Bi2O3 with electronic interaction between the oxide and the polymer chain of the polymer. The GE/α-Bi2O3@PPy composite electrode (type I supercapacitor) displayed a predominantly capacitive profile with low impedance values and good electrochemical stability after 50 charge and discharge cycles. The specific capacitance of α-Bi2O3 @PPy composite was found in the range of 634 to 301 F g-1 to gravimetric current of 3 and 10 A g-1, respectively.
| Main Authors: | , , , , , , , |
|---|---|
| Format: | Digital revista |
| Language: | English |
| Published: |
Sociedade Brasileira de Química
2019
|
| Online Access: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-50532019000400727 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | New composite based on polypyrrole (PPy) and bismuth oxide (α-Bi2O3) was investigated as supercapacitor electrode. The α-Bi2O3 was obtained by hydrothermal route at 500 ºC for 2 h. Cyclic voltammetry was used to electropolymerize PPy on graphite electrode (GE) or on GE/α-Bi2O3. The X-ray diffraction profile of Bi2O3 revealed the α-Bi2O3 monoclinic structure with space group P21/c.The scanning and transmission electron microscopy images showed that PPy coated α-Bi2O3. Raman spectra showed that PPy inhomogeneously coated α-Bi2O3, but it was still possible to obtain a α-Bi2O3 @PPy core-shell hybrid composite with highly ordered α-Bi2O3 with electronic interaction between the oxide and the polymer chain of the polymer. The GE/α-Bi2O3@PPy composite electrode (type I supercapacitor) displayed a predominantly capacitive profile with low impedance values and good electrochemical stability after 50 charge and discharge cycles. The specific capacitance of α-Bi2O3 @PPy composite was found in the range of 634 to 301 F g-1 to gravimetric current of 3 and 10 A g-1, respectively. |
|---|