Use of Natural Rubber Membranes as Support for Powder TiO2and Ag/TiO2 Photocatalysts
The purpose of this study was to synthesize TiO2-polymer composites able to act as photocatalyst membranes. TiO2 catalysts were prepared using the sol-gel method to contain 0.0, 0.5, 1.0, and 2.0 wt.% of embedded Ag particles, subsequently incorporated into natural rubber latex at a weight fraction of 15%. Samples of these ceramic powders were suspended in a latex emulsion (natural rubber), cast in Petri dishes and slowly dried in an oven. The resulting materials were evaluated by X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray, diffuse reflectance spectroscopy, differential scanning calorimetry, thermogravimetry, and photocatalytic assaying using methylene blue as an organic pollutant reference. All composite membranes exhibited good photoactivity conferred by TiO2 powder, with 98% dye fading after 300 min of ultraviolet irradiation.
Main Authors: | , , , , , , , |
---|---|
Format: | Digital revista |
Language: | English |
Published: |
Sociedade Brasileira de Química
2016
|
Online Access: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-50532016000300575 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The purpose of this study was to synthesize TiO2-polymer composites able to act as photocatalyst membranes. TiO2 catalysts were prepared using the sol-gel method to contain 0.0, 0.5, 1.0, and 2.0 wt.% of embedded Ag particles, subsequently incorporated into natural rubber latex at a weight fraction of 15%. Samples of these ceramic powders were suspended in a latex emulsion (natural rubber), cast in Petri dishes and slowly dried in an oven. The resulting materials were evaluated by X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray, diffuse reflectance spectroscopy, differential scanning calorimetry, thermogravimetry, and photocatalytic assaying using methylene blue as an organic pollutant reference. All composite membranes exhibited good photoactivity conferred by TiO2 powder, with 98% dye fading after 300 min of ultraviolet irradiation. |
---|