Desproporcionamento de tolueno sobre zeólitas tipo mordenita - atividade e seletividade na obtenção de xilenos
A sodium mordenite zeolite (Na-MOR) was synthesized and modified by dealumination with chloridric acid solution (H-MOR). X-Ray Diffraction (XRD), Inductive Coupled Plasm (ICP) and Scanning Electron Micrograph (SEM) techniques were used for sample characterization. The zeolite catalytic behavior was evaluated through toluene disproportionation at 435°C. It was verified that mordenites were very selective for the disproportionation reaction and the samples with higher aluminum content showed larger initial activity, however, these samples showed too a higher deactivation velocity due to a blockage of the unidimensional porous system of the zeolite by coke deposits. The selectivity to xylene isomers was practically not influenced by the Si/Al ratio and changed with the time on stream, due to coke formation. Transition state shape selectivity inside the mordenite pores is also discussed.
| Main Authors: | , , |
|---|---|
| Format: | Digital revista |
| Language: | Portuguese |
| Published: |
Sociedade Brasileira de Química
2000
|
| Online Access: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0100-40422000000300003 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | A sodium mordenite zeolite (Na-MOR) was synthesized and modified by dealumination with chloridric acid solution (H-MOR). X-Ray Diffraction (XRD), Inductive Coupled Plasm (ICP) and Scanning Electron Micrograph (SEM) techniques were used for sample characterization. The zeolite catalytic behavior was evaluated through toluene disproportionation at 435°C. It was verified that mordenites were very selective for the disproportionation reaction and the samples with higher aluminum content showed larger initial activity, however, these samples showed too a higher deactivation velocity due to a blockage of the unidimensional porous system of the zeolite by coke deposits. The selectivity to xylene isomers was practically not influenced by the Si/Al ratio and changed with the time on stream, due to coke formation. Transition state shape selectivity inside the mordenite pores is also discussed. |
|---|