Evaluation of the surface roughness of a nanofilled composite resin submitted to different smoothing and finishing techniques
Abstract Introduction: Controlling the surface smoothness characteristics of the composite resin when performing a direct restorative technique is one of the factors involved in achieving restorative success. Objective: The purpose of this study was to evaluate the surface roughness of a nanofilled composite resin submitted to different smoothing and finishing techniques. Material and method: Fifty test specimens were made with the Z350 XT composite resin (3M ESPE) and then divided into five study groups according to the smoothing and finishing method applied, as follows: G1 (control), polyester strip; G2, composite spatula; G3, brush cleaned with absolute alcohol and dried; G4, brush cleaned with absolute alcohol, dried and moistened with Single Bond (3M ESPE); and G5, brush cleaned with absolute alcohol, dried and moistened with Natural Glaze surface sealant (DFL). After fabrication, the specimens were stored for 24 h in deionized water. The surface roughness of the specimens was measured using a profilometer. Surface roughness means were compared by analysis of variance followed by Tukey’s test at a level of significance of 5%. Result: The lowest surface roughness was observed in G1 (control group) and the highest, in G3. G5 had lower surface roughness values compared to the other test groups, and presented values similar to those of the control group. Conclusion: The smoothing and finishing techniques influenced the surface roughness of the composite resin. Application of the surface sealant by the copolymerization technique resulted in lower roughness values. The use of a clean, dry brush promoted roughness values beyond the acceptable limit, and is therefore liable to compromise the performance of composite resin restorations.
| Main Authors: | , , , , |
|---|---|
| Format: | Digital revista |
| Language: | English |
| Published: |
Universidade Estadual Paulista Júlio de Mesquita Filho
2016
|
| Online Access: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1807-25772016000200110 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|