Effects of etching and adhesive applications on the bond strength between composite resin and glass-ionomer cements
OBJECTIVE: This study determined the effects of various surface treatment modalities on the bond strength of composite resins to glass-ionomer cements. MATERIAL AND METHODS: Conventional (KetacTM Molar Quick ApplicapTM) or resin-modified (PhotacTM Fil Quick AplicapTM) glass-ionomer cements were prepared. Two-step etch-rinse & bond adhesive (AdperTM Single Bond 2) or single-step self-etching adhesive (AdperTM PromptTM L-PopTM) was applied to the set cements. In the etch-rinse & bond group, the sample surfaces were pre-treated as follows: (1) no etching, (2) 15 s of etching with 35% phosphoric acid, (3) 30 s of etching, and (4) 60 s of etching. Following the placement of the composite resin (FiltekTM Z250), the bond strength was measured in a universal testing machine and the data obtained were analyzed with the two-way analysis of variance (ANOVA) followed by the Tukey's HSD post hoc analysis (p=0.05). Then, the fractured surfaces were examined by scanning electron microscopy. RESULTS: The bond strength of the composite resin to the conventional glass-ionomer cement was significantly lower than that to the resin-modified glass-ionomer cement (p<0.001). No significant differences were determined between the self-etching and etch-rinse & bond adhesives at any etching time (p>0.05). However, a greater bond strength was obtained with 30 s of phosphoric acid application. CONCLUSIONS: The resin-modified glass-ionomer cement improved the bond strength of the composite resin to the glass-ionomer cement. Both etch-rinse & bond and self-etching adhesives may be used effectively in the lamination of glass-ionomer cements. However, an etching time of at least 30 s appears to be optimal.
| Main Authors: | , , |
|---|---|
| Format: | Digital revista |
| Language: | English |
| Published: |
Faculdade De Odontologia De Bauru - USP
2012
|
| Online Access: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572012000600008 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|