Copolymerization of 1-hexene and 1-dodecene with 1,3-butadiene by a versatate/diisobutylaluminum hydride/t-butyl chloride catalyst system
The aim of this study was to incorporate an alpha-olefin (1-hexene or 1-dodecene) in a high cis polybutadiene chain, using a neodymium versatate/diisobutylaluminum hydride/t-butyl chloride catalyst system. The influence of alpha-olefin on polymerization reaction and polymer characteristics, using different weight ratios of butadiene/α-olefin, was evaluated. The copolymers were characterized by SEC, FTIR, NMR, TGA and viscosimetric analysis. The thermal stability of the polymer tended to increase with incorporation of alpha-olefins, while its microstructure was not affected. The weight average molecular mass (Mw) tended to increase and the polymerization conversion tended to decrease with increasing alpha-olefins content. The copolymers showed a lower intrinsic viscosity than for the homopolymer. The results indicated that the alpha-olefins were incorporated in the polybutadiene chain.
| Main Authors: | , , , , |
|---|---|
| Format: | Digital revista |
| Language: | English |
| Published: |
Associação Brasileira de Polímeros
2014
|
| Online Access: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0104-14282014000200004 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The aim of this study was to incorporate an alpha-olefin (1-hexene or 1-dodecene) in a high cis polybutadiene chain, using a neodymium versatate/diisobutylaluminum hydride/t-butyl chloride catalyst system. The influence of alpha-olefin on polymerization reaction and polymer characteristics, using different weight ratios of butadiene/α-olefin, was evaluated. The copolymers were characterized by SEC, FTIR, NMR, TGA and viscosimetric analysis. The thermal stability of the polymer tended to increase with incorporation of alpha-olefins, while its microstructure was not affected. The weight average molecular mass (Mw) tended to increase and the polymerization conversion tended to decrease with increasing alpha-olefins content. The copolymers showed a lower intrinsic viscosity than for the homopolymer. The results indicated that the alpha-olefins were incorporated in the polybutadiene chain. |
|---|