Stability of L minus sign[plus sing] - ascorbic acid in alginate edible films loaded with citric acid for antioxidant food preservation
Alginate of known copolymer composition was applied to antioxidant film developed by loading Lminus sign [plus sign] -ascorbic [AA] and citric [CA] acids. Relative humidity [RH, 33.3e75.2 per cent] of storage [25.0 °C] and glycerol [plasticizer] level, separately and through their interaction, decreased the AA hydrolytic stability and, hence, the antioxidant half-life of films. Glycerol can facilitate the water penetration from the environment into the polymeric network. The CA content did not vary during film storage. Film browning was then associated to AA degradation. However, CA slowed down the browning development at longer storage times because of the changes in the kinetic order. It may catalyze the formation of unstable color compounds. The present work permitted to determine that AA and CA were 100 per cent recovered after film casting. Also, it allowed finding the adequate film composition and period where the alginate film supporting AA and CA can be used as an antioxidant active interface for food preservation.
| Main Authors: | , , , , , |
|---|---|
| Format: | Texto biblioteca |
| Language: | eng |
| Subjects: | CITRIC ACID, ASCORBIC ACID HYDROLYSIS, GLYCEROL, ALGINATE COPOLYMER, ANTIOXIDANT FILMS, |
| Online Access: | http://ceiba.agro.uba.ar/cgi-bin/koha/opac-detail.pl?biblionumber=47364 http://ceiba.agro.uba.ar/cgi-bin/koha/opac-detail.pl?biblionumber= |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Alginate of known copolymer composition was applied to antioxidant film developed by loading Lminus sign [plus sign] -ascorbic [AA] and citric [CA] acids. Relative humidity [RH, 33.3e75.2 per cent] of storage [25.0 °C] and glycerol [plasticizer] level, separately and through their interaction, decreased the AA hydrolytic stability and, hence, the antioxidant half-life of films. Glycerol can facilitate the water penetration from the environment into the polymeric network. The CA content did not vary during film storage. Film browning was then associated to AA degradation. However, CA slowed down the browning development at longer storage times because of the changes in the kinetic order. It may catalyze the formation of unstable color compounds. The present work permitted to determine that AA and CA were 100 per cent recovered after film casting. Also, it allowed finding the adequate film composition and period where the alginate film supporting AA and CA can be used as an antioxidant active interface for food preservation. |
|---|