Corrosion resistance enhancement of SAE 1020 steel after Chromium implantation by nitrogen ion recoil
SAE 1020 construction steel is widely used as mortar reinforcement and small machine parts, but aside good surface properties as high ductility, hardness and wear resistance, its surface is prone to severe corrosion. As it is known, Chromium in amount over 12%-13% in the Fe alloys renders them resistance to several corrosive attacks. SAE 1020 samples were recovered with Chromium film and then bombarded either by nitrogen Ion Beam (IB) or Plasma Immersion Ion Implantation (PIII) to recoil implant Cr atoms in the Fe matrix. Samples treated by 100 keV N+ IB showed irregular, thin Cr profile, remaining a part of the film on the surface, to about 10 nm. Samples treated by 40 kV N PIII presented Cr layer of about 18% at., ranging to around 90 nm. Cr of the film was implanted in the Fe matrix in an almost flat profile. Results of corrosion test showed good performance of the PIII treated sample. The IB treated sample showed some enhancement over the non-treated reference and the only Cr film deposited sample showed no modification on the corrosion behavior as compared to the non-treated reference sample.
| Main Authors: | , , , , |
|---|---|
| Format: | Digital revista |
| Language: | English |
| Published: |
ABM, ABC, ABPol
2005
|
| Online Access: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392005000400005 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|