Electro chemical characterization of V X NbY C Z/BiX TiY O Z coatings produced through thermo-reactive diffusion and the sputtering technique
We present an experimental study of the structural evolution of a bilayer V X NbY C Z /Bix TiY O Z coating produced via thermo-reactive diffusion (TRD) and the RF sputtering process on D2 steel substrate. The TRD treatments were carried out in a molten mixture consisting of borax, ferro-niobium, ferro-vanadium, and aluminum, at 1313 K for 3 hours, using a resistance-heating furnace. BiX TiY O Z coatings were deposited using RF magnetron sputtering on TRD coatings, in order to carry out a study of the corrosion behavior of this compound. The crystallographic structure of the coatings was determined via X-ray diffraction (XRD), the corrosion resistance was analyzed through the po-tentiodynamic polarization test (Tafel Extrapolation) and electrochemical impedance spectroscopic analysis (EIS). XRD patterns showed that the ternary coating (VNbC2) was preferentially oriented along the [200] direction with a cubic-centered face structure, and the BiX TiY O Z coatings were amorphous. The electrochemical studies showed that the resistance corrosion of the coatings increased with respect to the bare substrate, and that polarization resistance in the bilayer coatings increased with respect to the ternary coatings, suggesting that the titanate has anticorrosive barrier effects.
| Main Authors: | , , |
|---|---|
| Format: | Digital revista |
| Language: | English |
| Published: |
Sociedad Mexicana de Física
2016
|
| Online Access: | http://www.scielo.org.mx/scielo.php?script=sci_arttext&pid=S0035-001X2016000200008 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|